Crosslink Material With High Impact Strength For Rotomoulding Material

Crosslink Material With High Impact Strength For Rotomoulding Material is an ultra-high strength cross-linked high-density polyethylene modified rotational molding powder with a cross-linking degree of Achieve 70-75%. XHPE065P uses peroxide cross-linking technology and cannot be used for medical,Food and other industries.

Model:XHPE065P

Send Inquiry

Product Description

Crosslink Material With High Impact Strength For Rotomoulding Material, XHPE065P is an ultra-high strength cross-linked high-density polyethylene modified rotational molding powder with a cross-linking degree of Achieve 70-75%. XHPE065P uses peroxide cross-linking technology and cannot be used for medical,Food and other industries.

Forms	● Commercially Available
Availability	● AS
Additive	● HS
Features	● Hightemperature ● Resistanceto cracking ● Impact resistance ● High rigidity
Uses	● High Temperature TANKS ● Pressurevessel
Agency Ratings	● ROHS
Packaging	● 20Kg / packaging
Shelf Life	● 1 years from the date of production

Datasheet	Typical Values	Unit	Test Method
● Physical
Density	0.948	g/cm3	ISO1183
Bulk Density	0.320	g/cm3	ISO60
Melt Index(190℃,2.16Kg)	NA	g/10min	ISO1133
Dry Flow Rate	24	s/100g	ARM
E.S.C.R.	≥1000	h	ASTM D1693
Melting Point	131	℃	ISO11357
● Mechanical
Tensile Strength at Break	22	MPa	ISO527
Tensile Elongation at Yield	240	%	ISO527
Flexural Modulus	1100	MPa	ISO178
impact Strength	35	J/mm	ARM
Hardness,Shore D	69	D	ISO868
● Thermal
Deflection Temperature(0.45MPa)	80	℃	ISO75
Vicat Softening Point	126	℃	ISO306
Brittleness Temperature	≤-70	℃	ISO974
● Aging
Oxidation Induction Time	60	min	ISO11357
UV Rating	2000	h	ASTM 2565
● Other
SurfaceResistivity	1017	Ω	IEC60093
Flame retardant	V2	Grade	UL-94